| POM M25S 日本宝理 |
| 规格级别： | 注塑级 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | 特性：共聚甲醛，高粘度 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||
| 物理性能 | 比重 | --- | ASTM D-792 | 1.41 | --- | ||||||||
| 机械性能 | 拉伸强度 | --- | ASTM D-638 | 60 | MPa | ||||||||
| 伸长率 | --- | ASTM D-638 | 75 | % | |||||||||
| 弯曲强度 | --- | ASTM D-790 | 96 | MPa | |||||||||
| 弯曲模量 | --- | ASTM D-790 | 2580 | MPa | |||||||||
|
--- |
|
|
|
|||||||||
| 电气性能 | 介电穿击强度 | 短时间实验：2mmt | ASTM D-149 | 24 | MV/m | ||||||||
| 体积电阻系数 | 3mmt | ASTM D-257 | 1×1014 | Ω.cm | |||||||||
| 热 性 能 | 线膨胀系数 | 室温 | --- | 10 | X10-5/°C | ||||||||
| 热变形温度 | 1.82MPa | ASTM D-648 | 110 | °C | |||||||||
| 阻燃性 | --- | UL 94 | HB | --- | |||||||||