| PA66 101L 美国杜邦 |
| 规格级别： | 注塑级 | 外观颜色： | --- |
| 用途概述： | 用于机械零件、消费用品等 | ||
| 备注说明： | 特性：改进机器进料和脱模特性。 | ||
| 性能项目 | 试验条件[状态] | 测试方法 |
|
数据单位 | |||||
| 基本性能 | 吸水率 | 24小时浸渍(23℃) | ASTM D-570 |
|
% | ||||
| 吸水率 | 饱和(23℃) | ASTM D-570 |
|
% | |||||
| 物理性能 | 比重 | --- | ASTM D-792 |
|
--- | ||||
| 泰伯磨耗量 | cs-17 Wheel,1000g | --- |
|
mg/1000 cycles | |||||
| 机械性能 | 硬度计硬度 | --- | ASTM D-676 |
|
--- | ||||
| 洛氏硬度M | --- | ASTM D-785 |
|
--- | |||||
| 洛氏硬度R | --- | ASTM D-785 |
|
--- | |||||
| 拉伸强度 | 23℃ | ASTM D-638 |
|
MPa | |||||
| 屈服强度 | 23℃ | --- |
|
MPa | |||||
| 断裂伸长率 | 23℃ | ASTM D-638 |
|
% | |||||
| 屈服伸长率 | --- | ASTM D-638 |
|
% | |||||
| 剪切强度 | 23℃ | ASTM D-732 |
|
MPa | |||||
| 揉曲模量 | 23℃ | ASTM D-790 |
|
MPa | |||||
| 1%形变时的压应力 | --- | ASTM D-695 |
|
MPa | |||||
| 埃佐冲击强度 | 23℃ | ASTM D-256 |
|
j/m | |||||
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 |
|
KJ/m2 | |||||
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 |
|
KJ/m2 | |||||
| 电气性能 | 耗散因数 | 106Hz(cps) | ASTM D-150 |
|
--- | ||||
| 体积电阻率 | --- | ASTM D-257 |
|
Ω.cm | |||||
| 介电常数 | 100Hz(cps) | ASTM D-150 |
|
--- | |||||
| 介电常数 | 103Hz(cps) | ASTM D-150 |
|
--- | |||||
| 介电常数 | 106Hz(cps) | ASTM D-150 |
|
--- | |||||
| 耗散因数 | 100Hz(cps) | ASTM D-150 |
|
--- | |||||
| 耗散因数 | 103Hz(cps) | ASTM D-150 |
|
--- | |||||
| 热 性 能 | 线性热膨胀系数 | --- | ASTM D-696 |
|
m/m/℃ | ||||
| 导热系数 | --- | --- |
|
w/mk | |||||
| UL可燃性导级 | --- | UL 94 |
|
--- | |||||
| 熔点 | Fisher Johns法 | ASTM D-789 |
|
℃ | |||||
| 熔点结晶 | --- | ASTM D-2177 |
|
℃ | |||||
| 脆化温度 | --- | ASTM D-746 |
|
℃ | |||||
| 热畸变温度 | 18×106Pa | ASTM D-648 |
|
℃ | |||||
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 |
|
℃ | |||||
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 |
|
% | |||||
| 其它性能 | 需氧指数 | --- | ASTM D-2863 |
|
% | ||||