| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
|
|
frame="void">
| ASTM D792 |
| ISO 1183 |
|
|
|
| 吸水率 |
immersion 24h;DAM |
ASTM D570 |
1.2 |
% |
| 吸水均衡性 |
50% RHL;DAM |
Similar to ISO 62 |
2.6 |
% |
|
|
|
frame="void">
| ASTM D570 |
| Similar to ISO 62 |
|
|
|
| 粘性系数测试 |
Viscosity Number;DAM |
ISO 307 |
275 |
cm3/g |
frame="void">
| 线型模量收缩率 |
- |
| - |
|
frame="void">
| Parallel;2.0mm;DAM |
| Flow;3.2mm(0.126in);DAM |
|
frame="void">
| ISO 294-4 |
| ISO 294-4 |
|
frame="void">
| 0.014 |
| 0.015 |
|
frame="void">
| cm/cm |
| cm/cm |
|
| 线型模量收缩率横向 |
2.0mm;DAM |
ISO 294-4 |
0.014 |
cm/cm |
| 机械性能 |
|
|
frame="void">
| ASTM D785 |
| ASTM D785 |
|
|
|
|
|
|
frame="void">
| ASTM D638 |
| ASTM D638 |
|
|
|
frame="void">
| 拉伸屈服强度 |
- |
| - |
| - |
|
frame="void">
| 50% RH |
| 50% RH |
| DAM |
|
frame="void">
| ISO 527 |
| ASTM D638 |
| ISO 527 |
|
|
frame="void">
| MPa |
| MPa |
| MPa |
|
|
|
frame="void">
| 50% RH |
| DAM |
| DAM |
|
frame="void">
| ASTM D638 |
| ISO 527 |
| ASTM D638 |
|
|
|
|
|
|
frame="void">
| ISO 527 |
| ISO 527 |
|
|
|
frame="void">
| 弯曲模量 |
- |
| - |
| - |
| - |
|
frame="void">
| 50% RH |
| 50% RH |
| DAM |
| DAM |
|
frame="void">
| ISO 178 |
| ASTM D790 |
| ISO 178 |
| ASTM D790 |
|
frame="void">
| 1.07 |
| 1.21 |
| 2.8 |
| 2.83 |
|
frame="void">
| GPa |
| GPa |
| GPa |
| GPa |
|
|
|
|
frame="void">
| ASTM D732 |
| ASTM D732 |
|
|
|
frame="void">
| IZOD缺口冲击 |
- |
| - |
|
|
frame="void">
| ISO 180/1A |
| ISO 180/1A |
|
|
frame="void">
| KJ/m2 |
| KJ/m2 |
|
|
|
|
frame="void">
| ASTM D256 |
| ASTM D256 |
|
|
|
frame="void">
| IZOD抗冲击强度 |
- |
| - |
|
|
frame="void">
| ISO 180/1U |
| ISO 180/1U |
|
|
|
frame="void">
| Charpy抗冲击强度 |
- |
| - |
|
|
frame="void">
| ISO 179/1eU |
| ISO 179/1eU |
|
|
|
frame="void">
| 低温下charpy缺口冲击 |
- |
| - |
|
frame="void">
| -30℃；50% RH |
| -30℃；DAM |
|
frame="void">
| ISO 179/1eU |
| ISO 179/1eU |
|
|
frame="void">
| J/cm2 |
| J/cm2 |
|
frame="void">
| 低温下charpy抗冲击强度 |
- |
| - |
|
frame="void">
| -30℃；50% RH |
| -30℃；DAM |
|
frame="void">
| ISO 179/1eU |
| ISO 179/1eU |
|
|
|
frame="void">
| Charpy缺口冲击 |
- |
| - |
|
|
frame="void">
| ISO 179/1eA |
| ISO 179/1eA |
|
|
frame="void">
| J/cm2 |
| J/cm2 |
|
| 拉力抗冲强度 |
Long specimen;DAM |
ASTM D1822 |
535 |
KJ/m2 |
|
|
|
frame="void">
| ASTM D256 |
| ASTM D256 |
|
|
|
| 电气性能 |
|
|
frame="void">
| IEC 60093 |
| IEC 60093 |
|
frame="void">
| 1e+011 |
| 1e+013 |
|
frame="void">
| ohm-cm |
| ohm-cm |
|
frame="void">
| 介电常数 |
- |
| - |
| - |
| - |
| - |
|
frame="void">
| 100Hz;50%RH |
| DAM |
| MHz;DAM |
| DAM |
| DAM |
|
frame="void">
| IEC 60250 |
| ASTM D150 |
| IEC 60250 |
| ASTM D150 |
| ASTM D150 |
|
frame="void">
| 10.03 |
| 3.6 |
| 3.6 |
| 3.9 |
| 4 |
|
|
frame="void">
| 介电常数 |
- |
| - |
| - |
| - |
| - |
|
frame="void">
| 1MHz;50%RH |
| 100Hz;DAM |
| 50%RH |
| 50%RH |
| 50%RH |
|
frame="void">
| IEC 60250 |
| IEC 60250 |
| ASTM D150 |
| ASTM D150 |
| ASTM D150 |
|
frame="void">
| 4.2 |
| 4.3 |
| 4.6 |
| 7 |
| 8 |
|
|
frame="void">
| 介电损耗因素 |
- |
| - |
| - |
| - |
|
frame="void">
| 100Hz;DAM |
| 100Hz;DAM |
| 1KHz;DAM |
| 1MHz;DAM |
|
frame="void">
| ASTM D150 |
| IEC 60250 |
| ASTM D150 |
| ASTM D150 |
|
frame="void">
| 0.01 |
| 0.015 |
| 0.02 |
| 0.02 |
|
|
| 加工性能 |
熔融温度 |
DAM |
--- |
280-300 |
℃ |
| 模量温度 |
DAM |
--- |
50-90 |
℃ |
| 干燥损失率 |
DAM |
--- |
Max0.05 |
% |
| 热 性 能 |
氧气指数 |
DAM |
ISO 4589-1/-2 |
28 |
% |
frame="void">
| ULRTI，电气性 |
- |
| - |
|
frame="void">
| 3.0mm;DAM |
| 1.5MM;DAM |
|
frame="void">
| UL 746B |
| UL 746B |
|
|
|
frame="void">
| ULRTI,抗冲性机械性能 |
- |
| - |
|
frame="void">
| 1.5mm;DAM |
| 3.0mm;DAM |
|
frame="void">
| UL 746B |
| UL 746B |
|
|
|
frame="void">
| ULRTI，机械性 |
- |
| - |
|
frame="void">
| 3.0mm;DAM |
| 1.5MM;DAM |
|
frame="void">
| UL 746B |
| UL 746B |
|
|
|
frame="void">
| 燃烧性 |
- |
| - |
| - |
| - |
| - |
| - |
|
frame="void">
| 1.5mm;DAM |
| 1.5mm;DAM |
| 0.71mm;DAM |
| 0.71mm;DAM |
| 3.0mm;DAM |
| 3.0mm;DAM |
|
frame="void">
| UL 94 |
| IEC 60695-11-10 |
| IEC 60695-11-10 |
| UL 94 |
| IEC 60695-11-10 |
| UL 94 |
|
frame="void">
| HB |
| HB |
| HB |
| HB |
| HB |
| HB |
|
frame="void">
| - |
| - |
| - |
| - |
| - |
| - |
|
frame="void">
| 热膨胀系数 |
线型20℃ |
| 线型20℃ |
|
frame="void">
| Parallel;23-55℃(73-130°F);DAM |
| Parallel;23-55℃(73-130°F);DAM |
|
frame="void">
| ASTM E831 |
| ISO 11359-1/-2 |
|
|
frame="void">
| μm/m-℃ |
| μm/m-℃ |
|
frame="void">
| 热膨胀系数 |
线型20℃下横流 |
| 线型20℃下横流 |
|
frame="void">
| 23-55℃(73-130°F);DAM |
| 23-55℃(73-130°F);DAM |
|
frame="void">
| ASTM E831 |
| ISO 11359-1/-2 |
|
|
frame="void">
| μm/m-℃ |
| μm/m-℃ |
|
|
|
frame="void">
| 10℃/min;DAM |
| DAM |
|
frame="void">
| ISO 11357-1-3 |
| ASTM D3418 |
|
|
|
frame="void">
| 变形温度 |
- |
| - |
| - |
| - |
|
frame="void">
| at 0.46 MPa |
| at 0.46 MPa |
| at 1.8 MPa |
| at 1.8 MPa |
|
frame="void">
| ISO 75-1/-2 |
| ASTM D648 |
| ASTM D648 |
| ISO 75-1/-2 |
|
frame="void">
| 200 |
| 210 |
| 65 |
| 70 |
|
|
| 脆化温度 |
DAM |
ASTM D746 |
-100 |
℃ |
| 其它性能 |
颜色 |
--- |
--- |
天然 |
--- |
| 形式 |
--- |
--- |
粒子 |
--- |
frame="void">
| 加工方法 |
- |
| - |
| - |
| - |
|
|
|
frame="void">
| 注塑成型 |
| 挤出 |
| 注塑 |
| 涂层 |
|
|