| PA66 CM3001-N 日本东丽工 |
| 规格级别： | 注塑级、标准级 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | 类型：尼龙-66未强化 | ||
| 性能项目 | 试验条件[状态] | 测试方法 |
|
数据单位 | |||||
| 基本性能 | 吸水率 | 23℃，24小时 | ASTM D-570 |
|
% | ||||
| 物理性能 | 比重 | --- | ASTM D-792 |
|
--- | ||||
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 |
|
mg/1000次 | |||||
| 机械性能 | IZOD冲击强度 | 23℃，V缺口1/2 | --- |
|
kg.cm/cm | ||||
| IZOD冲击强度 | 23℃，无缺口1/8 | --- |
|
kg.cm/cm | |||||
| 洛氏硬度 | 23℃ | ASTM D-785 |
|
R | |||||
| 洛氏硬度 | 23℃ | ASTM D-785 |
|
R | |||||
| 抗拉屈服强度 | -40℃ | ASTM D-638 |
|
Kg/cm2 | |||||
| 抗拉屈服强度 | 23℃ | ASTM D-638 |
|
Kg/cm2 | |||||
| 抗拉屈服强度 | 80℃ | ASTM D-638 |
|
Kg/cm2 | |||||
| 抗拉断裂强度 | 230℃ | ASTM D-638 |
|
Kg/cm2 | |||||
| 断裂伸长率 | 23℃ | ASTM D-638 |
|
% | |||||
| 挠曲强度 | -40℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 挠曲强度 | 23℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 挠曲强度 | 80℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 挠曲模量 | -40℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 挠曲模量 | 23℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 挠曲模量 | 80℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 压缩强度 | 23℃ | ASTM D-695 |
|
Kg/cm2 | |||||
| 抗剪强度 | 23℃ | ASTM D-732 |
|
Kg/cm2 | |||||
| IZOD冲击强度 | -40℃，V缺口1/2 | --- |
|
kg.cm/cm | |||||
| 电气性能 | 体积电阻率 | --- | ASTM D-257 |
|
Ω.cm | ||||
| 介电强度 | 1/8" | ASTM D-149 |
|
KV/mm | |||||
| 介电常数 | 50HZ | ASTM D-150 |
|
--- | |||||
| 介电常数 | 103Hz | ASTM D-150 |
|
--- | |||||
| 介电常数 | 106Hz | ASTM D-150 |
|
--- | |||||
| 损耗因素 | 50Hz | ASTM D-150 |
|
--- | |||||
| 损耗因素 | 103Hz | ASTM D-150 |
|
--- | |||||
| 损耗因素 | 106Hz | ASTM D-150 |
|
--- | |||||
| 抗电弧性 | 1/8" | ASTM D-150 |
|
--- | |||||
| IEC导电径踪指数 | --- | UL 746 |
|
V | |||||
| 热 性 能 | 线性热膨胀系数 | --- | ASTM D-696 |
|
10-5cm/cm | ||||
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 |
|
℃ | |||||
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 |
|
℃ | |||||
| UL-94抗燃级 | 1/16" | UL 94 |
|
--- | |||||
| 熔点 | --- | 差示扫描测热计DSC法 |
|
℃ | |||||
| 比热 | --- | --- |
|
Cal/g.°C | |||||
| 导热系数 | --- | --- |
|
Kcal/m.hr.° | |||||