| PC+ABS C1100 美国GE |
| 规格级别： | 注塑级 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | --- | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||||||||
| 机械性能 | 屈服抗拉强度 | --- | ASTM D638 | 55 | MPa | |||||||||
| 断裂拉伸应变 | --- | ASTM D 638 | 30 | % | ||||||||||
| 挠曲强度 | --- | ASTM D790 | 65 | MPa | ||||||||||
| 挠曲模量 | --- | ASTM D790 | 2300 | MPa | ||||||||||
| 加工性能 | 熔体温度 | --- | --- | 250-280 | ℃ | |||||||||
| 干燥温度 | --- | --- | 105-110 | ℃ | ||||||||||
| 干燥时间 | --- | --- | 3-4小时,最多8小时 | h | ||||||||||
| 模具温度 | --- | --- | 80-100 | ℃ | ||||||||||
| 热 性 能 |
|
--- |
|
|
|
|||||||||
| 其它性能 | 缺口伊佐德冲击值 | 23℃ | ASTM D 256 | 500 | J/m | |||||||||
| 比重 | --- | ASTM D792 | 1.12 | --- | ||||||||||
| 熔体流动速率 | 260℃，5kg | ASTM D 1238 | 8 | g/10min | ||||||||||
| 模塑收缩量 | 3.2毫米 | ASTM D955 | 5 to 7 | E-3 mm/mm | ||||||||||