| PBT SK603 美国杜邦 |
| 规格级别： | 玻璃纤维增强 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | 20%增强 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 机械性能 | 拉伸强度 | 23℃ | ASTM D-638 | 117 | MPa |
| 断裂伸长率 | 23℃ | ASTM D-638 | 3.3 | % | |
| 拉伸模量 | 23℃ | ASTM D-638 | 7482 | MPa | |
| 挠曲模量 | 23℃ | ASTM D-790 | 6137 | MPa | |
| 挠曲强度 | 23℃ | ASTM D-790 | 179 | MPa | |
| 埃佐缺口冲击强度(lzod) | 23℃ | ASTM D-256 | 69 | J/m | |
| 埃佐无缺口冲击强度(lzod) | 23℃ | ASTM D-4812 | 736 | J/m | |
| 电气性能 | 表面电阻率 | --- | ASTM D-257 | 0.016E15 | Ohm |
| 体积电阻率 | --- | ASTM D-257 | 2.3E15 | Ohm-cm | |
| 介电强度(短时) | 1.6mm/3.2mm | ASTM D-149 | 22/17 | Kv/mm | |
| 介电常数 | 1E3Hz/1E6Hz | ASTM D-150 | 3.8/3.6 | --- | |
| 耗电因数 | 1E3Hz/1E6Hz | ASTM D-150 | 0.006/0.019 | --- | |
| 加工性能 | 熔胶温度 | --- | --- | 240-260 | ℃ |
| 模温 | --- | --- | 30-130 | ℃ | |
| 干燥时间，除湿式干燥机 | --- | --- | 2-4 | h | |
| 干燥温度 | --- | --- | 110-130 | ℃ | |
| 加工湿度率 | --- | --- | ＜0.04 | % | |
| 热 性 能 | 熔融点 | --- | ASTM D-3418 | 225 | ℃ |
| 热变形温度 | 0.45MPa/1.8MPa | ASTM D-648 | 220/203 | ℃ | |
| 其它性能 | 比重 | --- | ASTM D-792 | 1.45 | --- |
| 收缩率 | 纵向/横向 | --- | 0.4-1.1 | % | |