透明阻燃PC
C2A技术数据（其中测试值为干态/湿态（RH50）数值）
|
性能项目
|
测试标准
|
测试条件
|
测试数据
|
数据单位
|
说明
|
|
|
物理性能
|
密度
|
ASTM D-792
|
---
|
1.2
|
g/cm3
|
透明阻燃PC特征：用磺酸盐类阻燃PC,无卤阻燃，达到韩国LG公司水平，通过欧盟最高环保标准。
透明阻燃PC用途：
用于电子电器部件， 阻燃电器仪表，开关防火外壳等
|
|
吸水率
|
ASTM D-570
|
24hr
|
0.14
|
%
|
||
|
线性成型收缩率
|
ASTM D-955
|
Flow,3.2mm
|
0.6
|
%
|
||
|
机械性能
|
熔体流动速率
|
ASTM D-1238
|
300℃,1.2Kg
|
15
|
g/10min
|
|
|
拉伸强度
|
ASTM D-638
|
---
|
65
|
MPa
|
||
|
断裂伸长率
|
ASTM D-638
|
---
|
6
|
%
|
||
|
屈服弯曲强度
|
ASTM D-790
|
6.4mm
|
89
|
MPa
|
||
|
弯曲模量
|
ASTM D-790
|
6.4mm
|
2300
|
MPa
|
||
|
悬臂梁缺口冲击强度
|
ASTM D-256
|
干湿不断裂
|
36
|
KJ/m2
|
||
|
烘干温度/时间
|
---
|
---
|
100/4-6
|
℃/hr
|
||
|
热性能
|
注塑成型温度范围
|
---
|
---
|
250-320
|
℃
|
|
|
注塑成型参考模温
|
---
|
---
|
90-110
|
℃
|
||
|
热变形温度
|
ASTM D-648
|
1.81MPa
|
127
|
℃
|
||
|
阻燃性
|
UL94
|
2.00mm
|
V-0
|
---
|
||
|
密度
|
ASTM D-792
|
---
|
1.2
|
g/cm3
|
||
|
吸水率
|
ASTM D-570
|
24hr
|
0.14
|
%
|
||
|
电性能
|
线性成型收缩率
|
ASTM D-955
|
Flow,3.2mm
|
0.6
|
%
|
|
|
熔体流动速率
|
ASTM D-1238
|
300℃,1.2Kg
|
15
|
g/10min
|
||
|
拉伸强度
|
ASTM D-638
|
---
|
65
|
MPa
|
||
|
断裂伸长率
|
ASTM D-638
|
---
|
6
|
%
|
||
注：上述数据为实验典型值，真实可靠。仅供参考，不作为正式质保承诺。