| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
吸水率 |
24hr，in 23℃ |
ASTM D-570 |
0.20 |
% |
| 物理性能 |
比重 |
--- |
JIS K-7112 |
1.20 |
--- |
| 透光率 |
3mm thick |
ASTM D-1003 |
88 |
--- |
| 折射率 |
--- |
ASTM D-542 |
1585 |
--- |
| 阻燃性 |
0.38mm |
UL 94 |
V-2 |
--- |
| 机械性能 |
frame="void">
| 拉伸强度 |
屈服点 |
| 断裂点 |
|
--- |
frame="void">
| ASTM D-638 |
| ASTM D-638 |
|
frame="void">
| 61(620) |
| 81(830) |
|
frame="void">
| Mpa(kgf/cm2) |
| Mpa(kgf/cm2) |
|
| 拉伸模量 |
--- |
ASTM D-638 |
2120(21600) |
Mpa(kgf/cm2) |
frame="void">
| 拉伸率 |
屈服点 |
| 断裂点 |
|
--- |
frame="void">
| ASTM D-638 |
| ASTM D-638 |
|
|
|
| 弯曲强度 |
--- |
ASTM D-790 |
90(915) |
Mpa(kgf/cm2) |
| 弯曲模量 |
--- |
ASTM D-790 |
2230(22700) |
Mpa(kgf/cm2) |
| 压缩强度 |
--- |
ASTM D-695 |
76(770) |
Mpa(kgf/cm2) |
| 耐冲击强度值 |
艾氏、带缺口厚度3.2mm |
ASTM D-256 |
880(90) |
J/m(kgf・cm/cm) |
| 耐冲击强度值 |
艾氏、带缺口厚度6.4mm |
ASTM D-256 |
140(14) |
J/m(kgf・cm/cm) |
| 洛氏硬度 |
--- |
ASTM D-785 |
77 |
M标度 |
| 电气性能 |
耐导电径迹性（CTI） |
--- |
IEC 112 |
300 |
V |
| 绝缘破坏强度 |
快速加压值厚度1.6mm |
ASTM D-149 |
30 |
kv/mm |
| 体积电阻率 |
--- |
ASTM D-257 |
3×1016 |
Ω.cm |
| 介电率 |
60Hz |
ASTM D-150 |
2.95 |
--- |
| 介电率 |
106Hz |
ASTM D-150 |
2.9 |
--- |
| 介电正切 |
60Hz |
ASTM D-150 |
0.0004 |
--- |
| 介电正切 |
106Hz |
ASTM D-150 |
0.009 |
--- |
| 耐电弧性 |
--- |
ASTM D-495 |
110 |
sec |
| 加工性能 |
frame="void">
| 成型收缩率 |
流动方向 |
| 垂直方向 |
|
--- |
frame="void">
| ASTM D-955 |
| ASTM D-955 |
|
frame="void">
| 0.5～0.7 |
| 0.5～0.7 |
|
|
| 热 性 能 |
负荷挠曲温度 |
负荷1.813MPa(18.6kgf/cm2) |
JIS K-7207 |
133 |
℃ |
| 负荷挠曲温度 |
负荷0.451MPa(4.6kgf/cm2) |
JIS K-7207 |
143 |
℃ |
frame="void">
| 线膨胀系数 |
流动方向 |
| 垂直方向 |
|
--- |
frame="void">
| ASTM D-696 |
| ASTM D-696 |
|
|
frame="void">
| 10-5cm/cm/℃ |
| 10-5cm/cm/℃ |
|
frame="void">
| 温度指数 |
电学式 |
| 冲击式 |
| 非冲击式 |
|
frame="void">
| 厚度1.47mm |
| 厚度1.47mm |
| 厚度1.47mm |
|
frame="void">
| UL 746B |
| UL 746B |
| UL 746B |
|
frame="void">
| 125 |
| 115 |
| 125 |
|
|