| PC PC-110 台湾奇美实业股份有限公司 物性数据 |
| 规格级别： | --- | 外观颜色： | --- |
| 用途概述： | 婴儿奶瓶、汽车警示灯亮、鼠标、巧克力盛装盒、高跟鞋、安全镜片等。 | ||
| 备注说明： | 特性：一般射出成型用 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||||
| 基本性能 | 熔体流动速率 | 300℃，1.2kg | ASTM D-1238 | 10 | g/10min | ||||||||||
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.20 | % | |||||||||||
| 物理性能 | 全光穿透率 | 3mmt | ASTM D-570 | 89 | % | ||||||||||
| 比重 | 23/23℃ | ASTM D-792 | 1.20 | --- | |||||||||||
| 浊度 | 3.2mmt | ASTM D-1003 | ＜0.8 | % | |||||||||||
| 机械性能 | 曲折率 | --- | ASTM D-542 | 1.585 | % | ||||||||||
| 降伏引张强度 | 23℃ | ASTM D-638 | 630 | kg/m2 | |||||||||||
|
|
|
|
|
|||||||||||
| 弯曲强度 | 23℃ | ASTM D-790 | 920 | kg/m2 | |||||||||||
| 弯曲模数 | 23℃ | ASTM D-790 | 24000 | kg/m2 | |||||||||||
| IZOD缺口冲击强度 | 1/4" | ASTM D-256 | 14.3 | kg.cm/cm | |||||||||||
| IZOD缺口冲击强度 | 1/8" | ASTM D-256 | 87 | kg.cm/cm | |||||||||||
| 洛氏硬度 | --- | ASTM D-785 | M-77 | M Scale | |||||||||||
| 压缩强度 | --- | ASTM D-695 | 780 | Kg/cm2 | |||||||||||
| 电气性能 | 体积电阻率 | --- | ASTM D-257 | 3 | ×1016Ω.cm | ||||||||||
| 介电常数 | 60Hz | ASTM D-150 | 2.95 | --- | |||||||||||
| 介电常数 | 106Hz | ASTM D-150 | 2.9 | --- | |||||||||||
| 介电损耗 | 60Hz | ASTM D-150 | 0.0004 | --- | |||||||||||
| 介电损耗 | 106Hz | ASTM D-150 | 0.009 | --- | |||||||||||
| 绝缘破坏强度 | 1.6mm | ASTM D-149 | 30 | KV/mm | |||||||||||
| 耐电弧性 | --- | ASTM D-495 | 110 | Sec | |||||||||||
| 加工性能 | 成型收缩率 | Across | ASTM D-955 | 0.5-0.7 | % | ||||||||||
| 成型收缩率 | Parallel | ASTM D-955 | 0.5-0.7 | % | |||||||||||
| 热 性 能 | 热传导系数 | --- | ASTM C-177 | 0.2 | W/m℃ | ||||||||||
| 维卡软化点 | 1Kg,50℃/hr | ASTM D-1525 | 153 | ℃ | |||||||||||
| 线膨胀系数 | 40～100℃ | ASTM D-696 | 6-8 | ×10-5cm/cm/℃ | |||||||||||
| 燃烧性 | 1/16" | UL 94 | V-2 | --- | |||||||||||
| 热变形温度 | 未退火,4.6Kg/cm2,120℃ | ASTM D-648 | 136 | ℃ | |||||||||||
| 热变形温度 | 未退火,18.6Kg/cm2,120℃ | ASTM D-648 | 125 | ℃ | |||||||||||